iglidur® V400 - Material data

Materials table

Genera l features	Unit	iglidur® V400	test method
Density	g/cm³	1,51
Colour		white
Max. humidity absorption at 23°C/50% R. H.	Wt.-%	0,1	DIN 53495
Max. water absorption	Wt.-%	0,2
Coefficient of surface friction, dynamic, against steel	μ	0,15-0,20
pv value, max. (dry)	MPa x m/s	0,50
Mechanical properties
Bending E-module	MPa	4.500	DIN 53457
Tensile strength at +20 °C	MPa	95	DIN 53452
compressive strength	MPa	47	DIN 53452
Maximum recommended surface pressure (20° C)	MPa	45
Shore D-hardness		74	DIN 53505
Physical and thermal properties
Max. long term application temperature	°C	+200
Max. short term application temperature	°C	+240
Minimum application temperature	°C	-50
thermal / heat conductivity	W/m x K	0,24	ASTM C 177
Coefficient of thermal expansion (at 23° C)	K^-1 x 10^-5	3	DIN 53572
Electrical properties
Specific forward resistance	Ωcm	> 10¹²	DIN IEC 93
Surface resistance	Ω	> 10¹²	DIN 53482
¹⁾ Without additional load; no gliding movement; relaxation not excluded.

'Table 01: Material Data

Fig. 01: Permissible pv values for iglidur® V400 plain bearings

iglidur® V400 plain bearings are not suitable for high pressures or static high loads. However they are characterized by a high wear resistance all the way up to the maximum recommended surface pressure.

Figure 02: Maximum recommended surface pressure dependent on the temperature (40 MPa to +20 °C)

X = Temperature [°C]
Y = Load [MPa]

Figure 03: Deformation under load and temperatures

X = Load [MPa]
Y = Deformation [%]

Mechanical properties

Maximum recommended surface pressure represents a mechanical material parameter. Tribological conclusions cannot be drawn from it. With increasing temperatures, the compressive strength of iglidur® V400 plain bearings decreases. Fig. 02 clarifies this connection.

Moreover the limit of the permitted loads at +100°C is still very high with 20 MPa. The high elasticity is also shown in Fig. 03.

Maximum surface speed

m/s	Rotating	Oscillating	Linear
Constant	0,9	0,6	2
Short-term	1,3	0,9	3

Permitted surface speeds

iglidur® V400 also permits high surface speeds due to the high temperature resistance. The very favorable coefficients of the bearing enable maximum surface speeds up to 1.5 m/s (0.8 m/s, continuous). Even higher are the permitted speeds for linear movement and 3 m/s can be attained on the short term.

Surface speed

p x v value and lubrication

Figure 20.3: Maximum recommended surface pressure dependent on the temperature

Temperatures

The long-term permissible maximum application temperature is +200°C. An additional securing is required at temperatures above 100°C. The wear resistance of the bearing is however excellent and claims a top position among all iglidur® materials. The compressive strength of iglidur® V400 plain bearings decreases with increasing temperatures. This connection can be seen in Fig. 02.

Temperatures, coefficient of thermal expansion

Figure 2.4: Coefficients of friction dependent on the surface speed, p = 0.75 MPa

Figure 05: Coefficients of friction dependent on the load, v = 0,01 m/s

X = Load [MPa]
Y = Coefficient of friction μ

Friction and wear

The coefficient of friction is dependent on the stressing of the bearing (Fig. 04 and 05). Furthermore, the coefficients of friction of iglidur® V400 are very constant. No other iglidur® bearing material exhibits a lower variance of the coefficients of friction, even when the shaft material is changed.

Coefficients of friction for iglidur® V400 against steel
(Ra = 1 µm, 50 HRC)

iglidur® V400	Dry	Grease	Oil	Water
Coefficients of friction µ	0,15 - 0,20	0,09	0,04	0,04

Coefficients of friction

Wear resistance

Fig. 06: Wear, rotating application with various

Figure 06: Wear, rotating application with different shaft materials, p = 1 MPa, v = 0,3 m/s

X = shaft materials
Y = wear [μm/km]

A = Aluminum, hard-anodized
B = machining steel
C = Cf53
D = Cf53, hard chrome-plated
E = St37
F = V2A
G = X90

Shaft materials

The influence of the shaft material on the wear resistance is greater than with the friction. Here already at low loads (0.75 MPa) there could be significant variations, as Figure 06 shows. In wear, the iglidur® V400 bearings additionally show better values in rotating applications than in swivelling motion (Fig. 07).

Shaft materials

Fig. 07: Wear in oscillating and rotating

Fig. 07: Wear with oscillating and rotating applications with Cf53 as a function of the load

X = Load [MPa]
Y = Wear [μm/km]

A = Cf53, rotating
B = Cf53, oscillating

Medium	Resistance
Alcohols	+
Hydrocarbons	+
Greases, oils without additives	+
Fuels	+
Diluted acids	+
Strong acids	+
Diluted bases	+
Strong bases	-

+ resistant 0 limited resistance - not resistant
All specifications at room temperature[+20 °C]
Table 05: Chemical resistance of the iglidur® bearings V400

Electrical properties

Specific forward resistance	> 10¹² Ωcm
Surface resistance	> 10¹² Ω

Chemical resistance

iglidur® V400 bearings have a good resistance against chemicals. They are resistant to cleaning agents, fats, oils, alcohol, solvents, diluted alkalis, as well as diluted acids.

The humidity absorption of the iglidur® V400 bearings amounts to just 0.2% with saturation in water.

Radioactive rays

iglidur® V400 bearings are resistant up to a radioactive intensity of 2 x 10⁴ Gy. Higher radiation affects the mechanical properties.

UV-resistant

iglidur® V400 bearings are largely resistant to UV rays.

Vacuum

The iglidur® V400 bearings can be used in vacuum only restrictedly. A degassing takes place.

Electrical properties

iglidur® V400 bearings are electrically insulating.

Maximum moisture absorption
at +23 °C/50 % r.F.	0,1 weight-%
Max. water absorption	0,2 weight-%

Table 06: Moisture absorption

Effect of moisture absorption on plain bearings

Diagram 10: Effect of moisture absorption

X = Moisture absorption [weight %]
Y = Reduction of inside diameter [%]

humidity absorption / moisture absorption

The humidity absorption of the iglidur® V400 bearings amounts to just 0,2% with saturation in water.

Important tolerances for iglidur® V400 bearings according to ISO 3547-1 after the press-fit.

Diameter d1 [mm]	Shaft h9 [mm]	iglidur® V400 F10 [mm]	Housing H7 [mm]
Up to 3	0 - 0,025	+0,006 +0,046	0 +0,010
> 3 bis 6	0 - 0,030	+0,010 +0,058	0 +0,012
> 6 bis 10	0 - 0,036	+0,013 +0,071	0 +0,015
> 10 bis 18	0 - 0,043	+0,016 +0,086	0 +0,018
> 18 bis 30	0 - 0,052	+0,020 +0,104	0 +0,021
> 30 to 50	0 - 0,062	+0,025 +0,125	0 +0,025
> 50 bis 80	0 - 0,074	+0,030 +0,150	0 +0,030

Table 07: Important tolerances iaw. ISO 3547-1 after press-fitting.

Installation tolerances

iglidur® V400 plain bearings are standard bearings for shafts with h-tolerance (recommended minimum h9). The bearings are designed for press-fit in a housing with h7 tolerance. After the installation in a housing with nominal diameter, the inner diameter of the bearing automatically adjusts to the F10 tolerance. In certain dimensions the tolerance in dependence on the wall thickness deviates from this (See delivery program )

Ülke/Bölge

Ülkenizi seçtiğinizde size yerel teklifler ve bilgiler gösterilecektir.

Dil ayarları

Tercih edilen dili seçin:

Teslimat noktanızı seçin

iglidur® V400 - Material data

Materials table

Mechanical properties

Maximum surface speed

Permitted surface speeds

Temperatures

Friction and wear

Coefficients of friction for iglidur® V400 against steel(Ra = 1 µm, 50 HRC)

Shaft materials

Electrical properties

Chemical resistance

Radioactive rays

UV-resistant

Vacuum

Electrical properties

humidity absorption / moisture absorption

Important tolerances for iglidur® V400 bearings according to ISO 3547-1 after the press-fit.

Installation tolerances

Ülke/Bölge

Dil ayarları

Page not found

Alışveriş sepeti

Alışveriş sepeti

Coefficients of friction for iglidur® V400 against steel
(Ra = 1 µm, 50 HRC)